ASTM D 4065 - 06 Standard Practice for Plastics: Dynamic Mechanical Properties: Determination and Report of Procedures

American Society for Testing and Materials (ASTM). Current edition approved Dec. 1, 2006. Published December 2006. Originally
approved in 1982. Last previous edition approved in 2001 as D 4065 - 01. This practice is for general use in gathering and reporting dynamic mechanical data. It incorporates laboratory practice for determining dynamic mechanical properties of plastic specimens subjected to various oscillatory deformations on a variety of instruments of the type commonly called dynamic mechanical analyzers or dynamic thermomechanical analyzers. This practice is intended to provide means of determining the transition temperatures, elastic, and loss moduli of plastics over a range of temperatures, frequencies, or time, by free vibration and resonant or nonresonant forced vibration techniques. Plots of elastic and loss moduli are indicative of the viscoelastic characteristics of a plastic. These moduli are functions of temperature or frequency in plastics, and change
rapidly at particular temperatures or frequencies. The regions of rapid moduli change are normally referred to as transition regions. The practice is primarily useful when conducted over a range of temperatures from −160°C to polymer degradation and is valid for frequencies from 0.01 to 1000 Hz. This practice is intended for materials that have an elastic modulus in the range from 0.5 MPa to 100 GPa [73 psi to 1.5 3 107 psi].